粉煤灰综合利用 FLY ASH COMPREHENSIVE UTILIZATION 2015no.2 试验与应用 水玻璃激发粉煤灰、矿粉活性的试验研究 Experimental Study on Fly Ash and Slag Activated with Sodium Silicate 吴辉琴,张春,李青,吴超,户相洛 (广西科技大学土木建筑工程学院,广西,柳州,545006 摘要:以水泥为主要胶凝材料,掺加工业废渣粉煤灰、矿粉作为替代物,同时添加一定量的水玻璃激发剂,研究其 对矿物掺合料的激发机理及合理掺量。结果表明:水玻璃对矿物掺合料的活性激发效果表现良好,改善了水泥基材料的 强度,实现了保护环境和节约经济的目的。 关键词矿物掺合料;水玻璃;活性激发 中图分类号:TQ528.02 文献标识码:A 文章编号:1005-8249(2015)02-0023-03 WU Hui-qin ,ZHANG Chun ,LI Qing ,HU Xiang-luo WU Chao ( Collegeof Civil Engineering ,Guangxi University science and technology ,Liuzhou 545006 ,China ) Abstract :The stimulation mechanism of mineral admiatures and proper dosage of sodium silicate activators is studied .The results show that the sodium silicate on good activating effect of mineral admixtures and improve the strength of cement-based material .This method achieves the purpose of protecting environment and saving the economy . Key Words :Mineral admixture ;Sodium silicate ;Activation 粉煤灰和矿粉是比较典型的可以被激发剂激发而 文章在研制出一种矿粉-粉煤灰水泥基材料的基 发生水化、产生强度的胶凝材料。利用粉煤灰、矿粉取 础上41,针对该种水泥基材料,采取对粉煤灰物理细 代混凝土中的部分水泥和细集料,较好地改善混凝土 磨和添加水玻璃化学激发剂结合的方法,进一步通过 的某些性能并节约水泥,一直是人们研究、关注的课 实验研究粉煤灰、矿粉替代水泥胶凝材料制作轻型节 题,而发挥粉煤灰、矿粉的活性或活性成分,却是充分 能混凝土砌块时,水玻璃掺量对粉煤灰、矿粉及水泥组 利用粉煤灰和矿粉作用的关键...
水玻璃激发粉煤灰、矿粉活性的试验研究.pdf