粉煤灰综合利用 2012No.2 FLY ASH COMPREHENSIVE UTILIZATION 研究 热活化煤石-水泥复合体系水化性能分析 Research on Hydration Properties of Blended Cement based on Thermal Activated Coal Gangue 何燕 (同济大学材料科学与工程学院建筑材料研究所,上海201804) 要:采用比强度法对活化煤研石的火山灰效应进行评定,通过Ca(OH)2剩余量和化学结合水量的测定,分析活 化煤矸石水泥体系的水化程度,并采用X射线衍射分析,差热分析对其水化过程进行研究。结果表明:煅烧温度为 750℃,保温时间为4h的热活化煤矸石对水泥体系的火山灰贡献率较高;该体系Ca(OH)2剩余量较少,化学结合水量较 多,其水化产物主要以Cs凝胶,Ca(OH)2和钙矾石为主。 关键词:煤矸石热活化水化性能 中图分类号:TQ172.78*2 献标识码:文章编号:1005-8249(2012)02-0014 He Yan College Material Science and Technology ,Tongji University ,Shanghai 201804 ) Abstract :By specifie strength concept ,the pozzolanic effect of activated coal gangue could be investigated .Through the content of Ca ( )2surplus and the amount of chemically bined water ,the hydration degree of activated coal gangue-cement system could be investigatod . By means of X-ray diffraction and Differential Thermal Analysis etc ,the hydration process of the cement system with activated coal gangue could 化反应的早期其填充作用较明显,使集料与浆体的界 (3)磨细粉煤灰中<20m的颗粒粒径对其活性 面缺陷减少,致密性提高,大幅度提高了强度,进一步 影响较大,粉磨时间对抗折强度活性指数的影响比抗 延长粉磨时间则效果不显著;后期粉煤灰火山灰活性 压强度活性指数的影响较大,粉磨10min对7d抗压强 起主要作用,粉煤灰细度的减小,增加了粉煤灰颗粒的 度活性指数的影响较显著。 反应面积,使浆体中的水化产物增多,后期强度有一定 参考文献 程度的增加。 [1]文梓芸,钱春香等混...
热活化煤矸石-水泥复合体系水化性能分析.pdf