粉煤灰综合利用 FLY ASH COMPREHENSIVE UTILIZATION 2015NO.1 试验与应用 不同温度下锂渣混凝土的早期抗裂性能* Cracking Resistance at Early Ages of Concrete added with Lithium Slag under Different temperature 郭江华，侍克斌，吴福飞 (新疆农业大学水利与土木工程学院新疆乌鲁木齐830052) 摘要：针对新疆的特殊地理区域和矿渣资源，用刀口法对不同温度下锂渣混凝土早期抗裂进行了研究.试验结果 表明：锂渣掺量在一定范围内可以控制混凝土早期裂缝，且最优掺量为30%；高温时锂渣混凝土的耐久性优于素混凝土 的耐久性；锂渣水化产物的膨胀性能够补偿高性能混凝土的早期收缩，从而提高高性能混凝土的早期抗裂性能. 关键词：高性能混凝土；锂渣；不同温度；早期抗裂 中图分类号：TU528.2 文献标识码：A 文章编号：1005-8249(2015)01-0033-03 Guo Jianghua Shi Kebin Wu Fufei Abstract:In view of the special geography and slag resourees in Xinjiang the research on the early cracking resistance of lithium slag concrete under different temperature by using knife edge method.The experimental results show that:The dosages of lithium slag concrete cracks can be controlled in a certain range and the optimal dosage is 30%:durability in high temperature lithium slag concrete durability is better than that of plain concrete.Expansion of early shrinkage of high performance concrete can pensate the lithium slag hydration products so as to improve the early eracking resistance of high performance conerete. Key words:High performance concrete Lithium slag Different temperature the carly cracking resistance 混凝土材料因其可塑性好、强度高、粘聚性好等特缝2.新疆是温带大陆性气候，夏季炎热干旱，冬季 点，自问世以来便在建筑行业中大范围地使用.近些 寒冷干燥.由于新疆的这种特殊地域，通过以往的工 年随着高性能混凝土的出现，由于其力学性能稳定，早 程实践不难发现，在不同温度下浇筑的混凝土裂缝有 期强度高，具有较好的韧性和体积稳定性等性能，使得 着不同的差距，由于温度的急剧变化，普通混凝土在如 一些有难度的大跨高耸结构得以建成.与其他建 此的环境下服役，寿命降低是必然的. 筑材料一样，混凝土结构建筑物在建设和使用的过程 长久以来，国内外的很多专家和学者为研究混凝 中也存在着一些问...
不同温度下锂渣混凝土的早期抗裂性能.pdf