粉煤灰综合利用 FLY ASH COMPREHENSIVE UTILIZATION 2014N0.4 专题研究 再生骨料透水混凝土体积法配比设计关键参数的优化选择* Optimal Selection for Key Parameters of Porous Pervious Concrete made from Recycled aggregates's Mix Design with Method of Volume 龚平，张高波，周余 (长江大学城市建设学院，湖北荆州434023) 摘要：以再生骨料配制的透水生态混凝土为研究对象，用体积法进行配合比设计并调整不同的配比参数，研究保 证再生骨料配制透水生态混凝土透水性和强度的最佳配比参数，并比较再生骨料与天然骨料配比设计中参数选择的异同. 关键词：再生骨料；透水混凝土；体积法配比设计；抗压强度；透水系数 中图分类号：TU528.0 文献标识码：A文章编号：1005-8249(2014)04-0003-03 Gong Ping' Zhou Yu? (Civil Construction College of Yangtze University Hubei Jingzhou 434000 China Abstract:The porous pervious concrete made from recycled aggregates was selected as the object of study.With method of volume the mix design parameters of various ratios were adjusted to study out the optimal mix parameters to obtain good permeability and enough strength.The similarities and differences of the optimal mix parameters'selection between the concrete made of recycled aggregate and natural aggregate was pared. Key words:Recycled aggregates Porous pervious concrete;Mix design with method of volume;Compressive strength;Permeability coefficient; 透水混凝土配合比设计常用方法有质量法、体积 1原材料及试验方法 法和比表面法，再生骨料配制透水生态混凝土，成熟经 验较少，不适用利用经验图表的质量法，比表面积法以 1.1原材料 假设骨料颗粒为球形计算而得，而再生骨料为天然骨 水泥：P042.5水泥，华新水泥股份有限公司生 料破碎而成，表面与球形差异巨大，因而也不适用比表 产.粗骨料：由引江济汉荆州段实验试块C25废弃混 面积法.体积法是以原有粗骨料孔隙率为基础，依据 凝土试块人工破碎，粒径16mm~20mm.砂：建筑中 目标孔隙率经过详细计算，以控制填浆体积，采用体积 砂，细度模数2.36.减水剂：聚羧酸盐类高效减水剂， 法进行透水混凝土配合比设计的关键是对主要参数的 掺量2%~3%.水：自来水. 确定1.本文采用体积法进行配合比设计并调整不1.2试验方法 同的配比参数，以再生骨料配制的透水生态混凝土为 1.2.1成型方法成型方法为人工插捣...
再生骨料透水混凝土体积法配比设计关键参数的优化选择.pdf