粉煤灰综合利用 FLY ASH COMPREHENSIVE UTILIZATION 2011NO.1 试验特迹用 大掺量炉底渣在预拌砂浆中的应用研究 Application Study of Ready -mixed Mortar with High Furnace Bottom Slag 郭锋，钱中秋 (江苏尼高科技有限公司，江苏常州213141) 摘要：针对炉底渣在预拌砂浆中部分替代河砂进行了试验研究，在砂浆中复合使用表面活性剂与保水调化剂组 分，降低了炉底渣的蓄水量，测试了砂浆的工作性、抗压强度、粘接强度、抗开裂性能等基本性能指标.结果表明，该砂浆 可操作性良好，保水率、力学性能、收缩率等指标，完全满足国家相关标准的要求. 关键词：炉底渣；预拌砂浆；收缩率 中图分类号：TQ177.62 文献标识码：A 文章编号：1005-8249(2011)01-0027-04 GUO Feng QIAN Zhong-qiu (Jiansu Nigao Science and Technology Co.Lid.Changzhou 213141.Jiangsu China) Abstract:How to partly replace sand by furnace bottom slag in the ready-mixed mortar.Was tested the storage capecity of fumace bottom slag can be reduced by pounding surfactant and thickening powder in the mortar.The working perfomance pressive strength bond strength and anti-cracking peoperty of the mortar was tested.The results showed that the mortar had good manipuility and the water retention rate mechanical properties and shrinkage rate were fully meeting the requirements of relevant national standards. Key words fumace bottom slag:ready-mixed mortar;shrinkage rate 炉底渣是火力发电厂、城市集中供热系统等工业 1原材料与试验方法 和民用燃煤锅炉底部排出的粒径较粗的灰渣，一般为 碎石多孔结构，主要成分是SiO2、Al2O3和Fe2O3.炉 1.1原材料 底渣在各大发电厂、热电厂的日产量都相当大，一般每 原材料包括：P.042.5水泥（水泥的物理性质见 燃烧1t煤会产生1/3t炉底渣，目前炉底渣多限于砖 表1)、I级粉煤灰（主要化学成分见表2）、（赣江砂， 瓦厂的再利用，这些应用技术相对比较落后，对炉底渣 全部烘干后通过3mm筛网，细度模数为2.8，堆积密 的利用率较低，不仅污染了环境，也造成了资源的极大 度为1482kg/m3)、炉底渣（取自国电常州发电有限公 浪费. 司，烘干后通过3mm筛网，细度模数为1.5，堆积密度 如果将炉底渣替代预拌砂浆中的掺合料或集料， 为787kg/m3)、保水稠化剂（江苏尼高科技有限公司 不仅能降低砂浆的生产成本，对解决炉底渣的利用难 生产的NK-L型保水稠化剂，具有保水、...
大掺量炉底渣在预拌砂浆中的应用研究.pdf