粉煤灰综合利用 FLY ASH COMPREHENSIVE UTILIZATION 2014NO.2 试验与应用 高强抗磨混凝土配制技术研究 Research on High Strength and Wear-resistant Concrete Preparation Technology 赵彦江，李双喜，陈蔚，杨永杰、王桑，王洁 (新疆农业大学水利与土木工程学院，乌鲁木齐市830052) 摘要：以不同掺合料品种、不同骨料级配、不同水胶比条件下，测试混凝土的强度及抗磨性能.通过试验研究发 现：混凝土水胶比控制在0.25以下，混凝土中掺加硅粉、膨胀剂，并将骨料最大粒径减小到20mm以下，混凝土具有优异 的抗磨性.可使山区性河道，泄水建筑物混凝土磨损减少，增加建筑物的使用年限. 关键词：混凝土；高强；抗磨性 中图分类号：TU502 文献标识码：A文章编号：1005-8249(2014)02-0025-03 Zhao yan-jiang Li shuang-xi Chen wei Yang yong-jie Wang shen Wang jie College of water conservancy and civil engineering of Xinjiang Agricultural University 830052) Abstract:In this paper under the condition of different varieties of admixture different aggregate gradation and different water/cement rati- o concrete strength and anti-wear performance is tested.Through experimental study it is found that:with water-binder ratio below 0.25 adding silicon powder expansive agent in concrete and the aggregate maximum particle size below 20 mm concrete has excellent abrasion resistance. Therefore it can reduce the wear of mountain aerotaxis river and outlet structure which prolongs service life. Key words:concrete;high strength;wear-resisting 山区间河道坡度大，河水往往挟带大量砂石，在这 泄水建筑物混凝土的抗冲磨问题，决定配制C60~C80 样的河道上修建的泄水建筑物混凝土结构常常受到砂 的高强高性能混凝土材料来解决此问题. 石冲击磨耗、水中滚石的巨烈撞击和高速水流磨损作 用，使得工程破坏严重，严重影响了建筑物的安全运 1原材料 行.泄洪建筑物采用何种抗磨材料，才能保证建筑物 水泥：采用新疆青松水泥有限公司42.5普通水 不被冲坏，增加建筑物的使用年限，是值得研究的 泥，3d抗压强度为25.1MPa 28d抗压强度为48.9MPa 问题. 安定性合格；硅粉：新疆研科公司生产，细度： 通常，混凝土的抗冲磨性好坏首先与混凝土的强 20000m2/kg Si02:90.6% 活性指数：116%；膨胀剂：北 度相关，抗压强度...
高强抗磨混凝土配制技术研究.pdf