粉煤灰综合利用 FLY ASH COMPREHENSIVE UTILIZATION 2013NO.5 专题研究 引气剂对混凝土性能的影响研究 Effects on Properties of Concrete added with Air Entraining Agents 高辉，张雄，张永娟 (同济大学先进土木工程材料教育部重点实验室，上海201804) 摘要：研究了引气剂对混凝土工作性、力学性能以及抗冻融性能的影响.结果表明：通过掺加引气剂增加新拌混 凝土含气量，可以改善混凝土的工作性.同时混凝土的冻融耐久性得以改善，气孔间距系数越小，混凝土的冻融耐久性 指数就越大.但是，引气剂的掺入降低了混凝土的强度，硬化混凝土平均孔径越小，越有利于减小因引气而造成的抗压 强度损失. 关键词：引气剂；混凝土；抗压强度；工作性；耐久性 中图分类号：TU528.042.4 文献标识码：A 文章编号：1005-8249(2013)05-0007-03 Gao Hui Zhang Xiong Zhang Yong-juan (Key Laboratory of Advanced Civil Engineering Materials of the Ministry of Education Tongji University Shanghai 201804 China) Abstract:Effects of air entraining agents AEA)on workability mechanical properties and freezing-thawing circle of concrete were studied in this paper.The results indicated that the workability and freezing-thawing circle performance of concrete added with AEA were improved:freez- ing-thawing durability increased with the decrease of spacing factor.But AEA decreased the pressive strength of ooncrete.For the hardened wurete the smaller the arerage pore size is the more wnducive to reduce the loss of pressive strength coused by AEA. Key words:air entraining agents;concrete;pressive strength:workability durability 在20世纪30年代，美国、日本、英国等就开始使 1试验原材料与试验方法 用引气剂.在美国，引气混凝土的应用已得到很大的 发展.这是由于随着美国公路交通的发展，混凝土公 1.1原材料 路路面破坏严重，尤其是冬天用食盐或氯化钙溶化公 水泥：安徽宁国海螺PⅡ52.5；细集料：中砂，细度 路路面冰雪时，对混凝土路面破坏更为严重.应用引 模数2.54；粗集料：选用了粒径为5mm~30mm 表面比 气剂在混凝土中引入合适的气泡（孔）是显著改善混 较粗糙且质地坚硬的玄武岩碎石；水：自来水；选用引 凝土和易性与耐久性的有效技术途径121.在混凝土 气剂分别为：SJ三萜皂甙引气剂（以A...
引气剂对混凝土性能的影响研究.pdf