2012年8月下 施工技术 第41卷第371期 CONSTRUCTION TECHNOLOGY 101 沥青混合料中掺加消石灰粉替代部分 矿粉施工质量控制 宋宗平 (中交一公局第三工程有限公司,北京100120) [摘要]为改善沥青与石料黏附性,提高沥青路面的抗水损害能力,在连盐高速公路下面层结构沥青混凝土混合料 中,以消石灰替代部分石灰岩矿粉(总量不超过混合料质量的2%)进行施工.介绍了消石灰粉替代部分矿粉进行 施工的工序、配合比设计、压实方案和施工控制要点,最终沥青混合料总体质量得到控制. [关键词]沥青;消石灰;矿粉;配合比设计 [中图分类号]TU7;U416.217 [文献标识码]A [文章编号]1002-8498(2012)16-0101-03 Quality Control of Asphalt Mixture with Hydrated Lime Changing Some Mineral Powder Song Zongping The Third Engineering Co.Ltd.of the First Highway Engineering Bureau of CCCC Beijing 100120 China) Abstract:Changing some mineral powder for hydrated lime in asphalt mixture at down layers of Lianyungang-Yancheng expressway is applied to improve the adhesion between asphait and pebbles and water damage resistance for asphalt pavement.The construction process mix proportion pacting scheme and construction control points of the method of changing some mineral powder for hydrated lime is introduced.The whole quality of asphalt mixture is controlled. Key words:asphalt;hydrated lime;mineral powder;mix proportion design 为改善沥青与石料黏附性,提高沥青路面的抗 AC-25S型沥青混凝土面层粗骨料试验结果合 水损害能力,在连盐高速公路下面层结构沥青混凝 格,满足规范要求,如表1所示. 土混合料中,以消石灰替代部分石灰岩矿粉(总量 表1AC-25S型沥青混凝土面层粗骨料试验结果 不超过混合料质量的2%).下面以沥青下面层(沥 Table 1 Test results of coarse aggregate on AC-25S 青混凝土类型AC-25S)为例进行阐述. asphalt concrete surface 1准备工作 指标 材料规范 吸水 试验结果 名称要求 率/% 1.1原材料技术要求 相对密度 1号料>2.5表观相对密度2.719 0.20 沥青下面层采用AH-70沥青;石料选用石灰 毛体积相对密度2.704 岩,骨料坚硬、清洁、干燥、无风化、无杂质、活性物 2号料>2.5 表观相对密度2.7260.42 毛体积相对密度2.697 质含量低;矿粉使用石灰岩矿粉,实测含水量< 0.1%;...
沥青混合料中掺加消石灰粉替代部分矿粉施工质量控制.pdf
![2配合比,压路机,武汉,江苏,沥青混合料,长江,学术文献](https://www.guifanku.com/wp-content/uploads/2023/10/thumb781181.jpg)