施工技术 2014年10月下 66 CONSTRUCTION TECHNOLOGY 第43卷第20期 D0I:10.7672/sgjs2014200066 钢结构工程现场负温焊接技术措施 邢海龙，刘健博 (中建一局钢结构工程有限公司，北京100070) [摘要]钢结构现场焊接是施工中的重点、难点之一，冬期负温度下的焊接质量控制更是钢结构施工企业面临的难 题.结合乌鲁木齐某工程实践，提出了负温焊接的质量通病和形成原因，总结了钢结构冬期焊接施工经验以及保 证钢结构负温焊接质量的技术措施. [关键词]钢结构；负温；焊接；技术措施 [中图分类号]TU758.163 [文献标识码]A [文章编号]1002-8498(2014)20-0066-02 Technical Methods for Negative Temperature Welding on Site of Steel Structures Xing Hailong Liu Jianbo China Construction First Division Steel Structure Engineering Co.Lad.Beijing 100070 China) Abstract:Welding on site is the difficulty for steel structures especially the welding under negative temperature.Combining with the practice of an engineering in Urumqi the quality problems and forming reasons of negative welding were put forward.The construction experiences and technical methods assuring welding quality were summarized. Key words:steel structures;negative temperature;welding;technical methods 1工程概况 响.淬硬倾向越大，越易产生裂纹.钢结构中采用 乌鲁木齐市属中温带干旱大陆性气候区，以气的钢材主要有两种：碳素结构和低合金结构钢，常 候干燥，降雨量小，冰冻期长，昼夜温差变化较大，见的钢结构材料中，碳素钢主要为Q235 低合金结 春、秋多风，夏季短促而炎热，冬季漫长且严寒为其构钢主要为Q345 Q390 Q420.低合金钢含有锰、 主要特征.乌鲁木齐新客站站房及雨篷相关工程钒等合金元素而具有较高强度.Q345 Q390 Q420 中，钢结构构件多为30 35 40 50 70mm厚钢板拼的屈服强度比Q235提高将近一半，抗拉强度也提 接、卷制、焊接而成，主构件材质多为Q345C 高不少.但抗拉强度提高时相对降低了塑性和韧 Q345GJC Q420GJC等低合金钢.由于乌鲁木齐新 性，对焊接结构来说增加了转脆倾向.焊接时，近 客站ZF标工程为兰新第二双线工程重要的配套工 缝区的加热温度很高，使奥氏体晶粒发生严重长 程，工期要求紧，为按期完成施工任务，进行冬期焊 大，当快速冷却时，粗大的奥氏体将转变为马氏体. 接施工. 由金属强度理论可知，马氏体是一种脆硬组织，发 2负温焊接的质量通病及其成因分析 生断裂时只消耗较低的能量.因此，焊接接头有马 1)根据以往施工经验，在进行钢结构冬期焊接 氏体存在时，裂纹易于形成...
钢结构工程现场负温焊接技术措施.pdf